Refrigerant releasing composite

ABSTRACT

A composite configured to release refrigerant therefrom comprises a substrate material comprising polarized fibers of glass, polyamide, phenylene sulfide, carbon or graphite having bonded thereon a metal compound comprising a complex compound of a polar gaseous refrigerant and a metal salt and/or a hydrated metal hydroxide and/or a metal hydroxide of a metal selected from the group consisting of alkali metal, alkaline earth metal, transition metal, zinc, cadmium, tin, aluminum, or two or more thereof, at a concentration of at least about 0.3 grams/cc of open substrate material volume, and a coating composition thereon configured to prevent release of internal gaseous refrigerant therethrough at ambient temperatures and pressure and capable of penetration of gaseous refrigerant therethrough from the composite interior at temperatures causing internal gas pressures of 15% or more above exterior pressure for such refrigerant release.

BACKGROUND OF THE INVENTION

Materials presently available for protecting vehicles, ammunition, solid, liquid or gaseous fuels, rockets, missiles and/or personnel from small arms projectile penetration or penetration from flying shrapnel, fire, directed energy, explosions and associated heat and the like are relatively expensive. Moreover, such materials do not have self cooling and/or fire extinguishing properties. The composites described herein are relatively inexpensive and cost-effective to manufacture, may be produced in almost any shape, size and thickness, and are recyclable. The composites are configured to release gaseous refrigerant at temperatures above about 150° F. and preferably much higher temperatures, thereby providing cooling and fire extinguishing properties. The composites have mechanical and structural integrity and may be used in conjunction with penetration resistant materials or, in some cases, can be designed to provide some penetration resistance.

SUMMARY OF THE INVENTION

The preferred composites described herein comprise a substrate material comprised of woven, layered or intertwined polarized strands of glass, polyamide, polyphenylene sulfide, carbon or graphite fibers on which a metal compound comprising a coordinated complex compound of a polar gas refrigerant and sorbent comprising a metal salt or a metal hydroxide is polar bonded on the surface of the fibers and/or strands at concentrations sufficient to form bridges of the metal compound between adjacent substrate strands and/or substrate fibers. Single or multiple layers of the metal compound bonded fibers are coated with a coating material capable of preventing release or escape or increase in concentration (e.g. water) of the internal gaseous refrigerant at external atmospheric or ambient pressure but which is capable of allowing penetration of the refrigerant at internal refrigerant pressures resulting in total internal pressure of at least about 15% or more above exterior atmospheric/ambient pressure. Panels comprising laminates or other shaped geometries may be produced using composite layers. When heat is imposed on the composite via fire, explosion, directed energy, combustion of gasoline, oil, other liquid or gaseous or solid fuels, rocket fuel or by a projectile breaching the exterior coating, causing a temperature increase of the bonded metal compound and a resulting increase in internal composite pressure, the composite releases refrigerant. Such refrigerant release will cool the composite and may prevent ignition of protected contents and/or personnel or extinguish a flame. Panels comprising multiple layers having different sorbents and/or different refrigerants with different refrigerant release temperature/pressure ranges may be produced to achieve thermal gradient refrigerant release at selected temperatures.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The unique refrigerant releasing composite products described herein are preferably fabricated from a substrate material comprising preferably woven or intertwined polarized strands or layered strands of the substrate. Such woven or intertwined substrate material incorporate or utilize elongated or continuous fibers such as fabrics or cloth or unwoven intertwined fiber materials such as yarn, rope or the like where the fibers or strands of fibers have been twisted or formed in a coherent form such as yarn or weaves of strands. Various or different weaving patterns may be used, preferably three-dimensional weaves which yield multi-directional strength characteristics as compared to two-dimensional weaves having anisotropic strength characteristics. The preferred substrate utilizes elongated and/or continuous fibers or filaments as opposed to chopped or loose fibers or strands in which there is no interlocking or structural pattern to the fibrous substrate in order to achieve good mechanical strength. However, non-woven fibers including mat, batting, felt or chopped or loose fiber materials are useful for the purpose of refrigerant release composites, but offer less mechanical strength or penetration protection. Suitable materials also include needle woven layers of substrate fiber strands. Alternatively, layers of elongated, substantially continuous fiber strands which have not been woven in a three-dimensional weave may be used. Successive layers of the fibers are preferably positioned along different axes so as to give the substrate strength in multiple directions. Moreover, such layers of non-woven fibers can be positioned between layers of woven fibers.

The substrate material of which the fiber strands are made include glass, polyamide, polyphenylene sulfide, carbon or graphite fibers. Glass fibers are a preferred fiber material, woven glass fibers being relatively inexpensive and woven glass fiber fabric easy to handle and process in preparing the composites. The glass fibers may be E-glass and/or S-glass, the latter having a higher tensile strength. Glass fiber fabrics are also available in many different weaving patterns which also makes the glass fiber material a good candidate for the composites. Carbon and/or graphite fiber strands may also be used. Polyamide materials or nylon polymer fiber strands are also useful, having good mechanical properties. Aromatic polyamide resins (aramid resin fiber strands, commercially available as Kevlar® and Nomex®) are also useful. Yet another useful fiber strand material is made of polyphenylene sulfide, commercially available as Ryton®. Combinations of two or more of the aforesaid materials may be used in making up the substrate, with specific layered material selected to take advantage of the unique properties of each of them. The substrate material, preferably has an open volume of at least about 30%, and more preferably 50% or more, up to about 95%. The specific substrate material selected and used as well as the percentage of open volume may depend on the expected uses, including environmental exposure conditions, substrate melting temperatures, and the like.

The surface of the fibers and fiber strands of the aforesaid substrate material must be sufficiently polarized to at least provide some bonding between the fiber and the absorbent crystals adequate to achieve the below loading densities. Polarized fibers are commonly present on commercially available fabrics, weaves or other aforesaid forms of the substrate. If not, the substrate may be treated to polarize the fiber and strand surfaces. The surface polarization requirements of the fiber, whether provided on the substrate by a manufacturer, or whether the fibers are treated for polarization, must be sufficient to achieve a loading density of the metal salt or hydroxide on the fiber of at least about 0.3 grams per cc of open substrate volume whereby the bonded metal compound bridges at least some adjacent fiber and/or adjacent strands of the substrate. Polarity of the substrate material may be readily determined by immersing or otherwise treating the substrate with a solution of the salt or hydroxide, drying the material and determining the weight of the metal compound polar bonded to the substrate. Alternatively, polar bonding may be determined by optically examining a sample of the dried substrate material and observing the extent of metal compound bridging of adjacent fiber and/or strand surfaces. Even prior to such bonding determination, the substrate may be examined to see if excessive oil or lubricant is present on the surface. Oil coated material will substantially negatively affect the ability of the substrate fiber surfaces to form an ionic, polar bond with a metal salt or metal hydroxide. If excessive surface oil is present, the substrate may be readily treated, for example, by heating the material to sufficient temperatures to bum off or evaporate most or substantially all of the undesirable lubricant. Oil or lubricant may also be removed by treating the substrate with a solvent, and thereafter suitably drying the material to remove the solvent and dissolved lubricant. Substrates may also be treated with polarizing liquids such as water, alcohol, inorganic acids, e.g., sulfuric acid.

The substrate may be electrostatically charged by exposing the material to an electrical discharge or “corona” to improve surface polarity. Such treatment causes oxygen molecules within the discharge area to bond to the ends of molecules in the substrate material resulting in a chemically activated polar bonding surface. Again, the substrate material should be mostly free of oil prior to the electrostatic treatment.

A sorbent for the polar gas refrigerant comprising metal salt, or metal hydroxide, is bonded to the surface of the polarized substrate material by impregnating, soaking, spraying, flowing, immersing or otherwise effectively exposing the substrate surface to the metal compound. A preferred method of bonding the sorbent to the substrate is by impregnating, soaking, or spraying the material with a liquid solution, slurry or suspension or mixture containing the metal salt or hydroxide followed by removing the solvent or carrier by drying, heating and/or by applying a vacuum. The substrate may also be impregnated by pumping a salt or hydroxide suspension, slurry or solution or liquid-salt mixture into and through the material. Where the liquid carrier is a solvent for the salt, it may be preferred to use a saturated salt solution for impregnating the substrate. However, for some cases, lower concentrations of salt or hydroxide may be used, for example, where necessitated or dictated to meet permissible loading densities. Where solubility of the salt or hydroxide in the liquid carrier is not practical or possible, substantially homogeneous dispersions may be used. Where an electrostatically charged substrate is used, the salt or hydroxide may be bonded by blowing or dusting the material with dry salt or hydroxide particles.

As previously described, it is necessary to bond a sufficient amount of metal salt or metal hydroxide on the substrate to achieve at least some bridging of the salt or hydroxide crystal structure between adjacent fibers and/or strands. A sufficient amount of salt or hydroxide is provided by at least about 0.3 grams per cc of open substrate volume, preferably at least about 0.4 grams per cc, and most preferably at least about 0.5 grams per cc of open substrate volume, which is between about 30% and about 95% of the untreated substrate volume, and preferably between about 50% and about 95%. Following the aforesaid treatment, the material is dried in equipment and under conditions to form a flat layer, or other desired size and shape using a mold or form. A dried substrate will readily hold its shape. Unless the solvent is also the refrigerant, drying to substantially eliminate the solvent, carrier fluid or other liquid is necessary, although small amounts of fluid, for example, up to 1-2% of solvent, can usually be tolerated without detriment to the strength or refrigerant holding capacity of the material. Drying and handling techniques for such solvent removal will be understood by those skilled in the art. If the solvent is also the refrigerant, the solvent removal may be stopped at the desired level of refrigerant content. The most preferred refrigerants are water and ammonia.

Typical mass percentages of refrigerant mass per dry sorbent mass are between about 5% and about 80%. Hydroxides commonly do not absorb ammonia and are limited to water refrigerant of just one or a few moles of water per mole of hydroxide. Exposure of these compounds to heat causes a rise in refrigerant pressure and can be employed to release the refrigerant in the typically endothermic process. Heats of reaction range form about 35 kJ/mol ammonia for relatively high vapor pressure ammoniated complex compounds to over 70 kJ/mol water for hydrated complex compounds and select ammoniated compounds and even higher for hydroxide hydrates and even higher for the reduction of hydroxides into oxides, such heats of reaction absorbing often over 100 kJ/mol of water.

Metal salts or hydroxides bonded to the substrate are alkali metal, alkaline earth metal, transition metal, zinc, cadmium, tin, aluminum, double metal salts of the aforesaid metals, and/or mixtures of two or more of the metal salts. The salts of the aforesaid metals are halide, nitrite, nitrate, oxalate, perchlorate, sulfate or sulfite. The preferred salts are halides, and preferred metals are strontium, magnesium, manganese, iron, cobalt, calcium, barium and lithium. The aforesaid preferred metal salts provide molecular weight/electrovalent (ionic) bond ratios of between about 40 and about 250.

Unless the solvent is identical to the refrigerant and was intentionally retained during the drying process, to form a coordinated complex compound of a bonded metal salt or hydroxide and a polar gaseous refrigerant, the substrate material having the bonded metal salt or hydroxide (sorbent) formed as previously described is treated with the selected gaseous refrigerant which becomes absorbed on the sorbent. Such absorption reactions and the coordinated complex compounds are described in substantial detail in U.S. Pat. Nos. 5,298,231, 5,441,716 and 6,224,842, the descriptions of which are incorporated herein by reference. The preferred polar gas to be absorbed onto the metal salt to form the compound is selected from ammonia and water. Other ligands, such as amines and alcohols are also possible, but usually less desirable due to their flammability and low heat of reaction resulting in a lesser cooling effect. Phosphine is another polar gaseous refrigerant that may be used in special circumstances because of its toxicity. The specific polar gas refrigerant to be absorbed on the specific sorbent will depend on the temperature range desired to trigger or initiate release of the polar gas to achieve the desired cooling effect on the composite at the time it is exposed to heat by fire, explosion, directed energy, fuel combustion or is hit by a bullet, shrapnel or other invasive material causing a temperature rise. For example, to extinguish a flame, water may be the preferred refrigerant to be released by the composite. When metal hydroxides are used water is the only practical refrigerant forming the related hydrates and with the additional release at the highest temperature converting the hydroxide into the corresponding oxide. However, complex compounds with water as the polar refrigerant and hydrated metal hydroxides commonly release water at higher temperatures compared to the temperatures at which more volatile refrigerants such as ammonia or amines are released. Where it is desired for relatively low temperature refrigerant release, for example, between about 150° F.-400° F., ammonia refrigerant is useful, whereby the ammoniated complex compounds as previously described may be used. Because different ammoniated complex compounds will release (desorb) ammonia at different temperatures, the specific metal salt (sorbent) as well as the coordination step of the ammoniated complex compound may be selected depending on the desired refrigerant release temperature. For higher temperature refrigerant release, for example, in the temperature range between about 200° F.-800° F., water may be the refrigerant absorbed on the metal salts to form the complex compounds. Complex compounds of different metal salts and water will release water at different temperatures as will complex compounds of one metal salt having different water coordination spheres or steps. Thus, the specific absorbents and/or refrigerants and/or complex compound coordination steps may be selected depending on the specific refrigerant release temperature range desired. For yet higher temperatures, the release of water from a hydrated metal hydroxide may be used, e.g., sodium, calcium or lithium hydroxide hydrates. For example, hydrated metal hydroxides may release water at temperatures above 300° F. up to 1,000° F. At even higher temperatures, metal hydroxides may release water by converting to the corresponding oxide at temperatures up to about 2,000° F. Some hydroxides, however, will melt at or below 2000° F. thus likely releasing water.

As described, since refrigerants are released at different temperature ranges depending on their ligand sphere or chemical bond, it may be desirable to form a composite having different layers or laminates of layers of metal compounds using the same or different refrigerants having selected different absorbents yielding different ligand coordinating complex compounds, or other metal compounds such as hydroxides. For example, different ammoniated complex compounds and/or different hydrated complex compounds and/or hydroxides and/or hydrated hydroxides may be used in different layers of a composite. Moreover, the composite may be configured so that successively higher (or lower) temperature refrigerant release complex compounds and/or hydroxides are used in successive layers of the composite structure. It may also be desirable to utilize different refrigerants in different successive layers of the compounds so as to achieve a selected successive release of refrigerants at progressively higher temperatures. Such composites comprise multiple layers with two or more different layers and two or more different metal compounds. Such different metal compounds are selected from different complex compounds comprising different metal salts with one refrigerant, different metal salts with different refrigerants, one metal salt with different refrigerants or one metal salt with different coordination spheres of one refrigerant; hydrated metal hydroxides; and metal hydroxides. A composite having combinations of the aforesaid metal compounds, e.g., between two and six different metal compounds, may be used to release refrigerants at any number of different successive temperatures. Thus, such composites having selected thermal profile or thermal refrigerant gradient may release refrigerant gas or gases at controllable conditions to provide cooling and extinguish flame at such selected different specific trigger temperature/pressure conditions. Preferred composites for such progressive temperature refrigerant release will incorporate an ammoniated complex compound and/or a hydrated complex compound, and/or a hydrated metal hydroxide, and/or a metal hydroxide. The benefits of such an effect, whether using different refrigerants, different sorbents or both at such different and progressive temperatures, or using a single refrigerant composite, will be evident. For example, containers, cylinders, boxes or cases made from such a composite may be used for protecting many kinds of ordnance or other valuable and/or fragile material such as ammunition, fuel and missiles as well as personnel.

Where the metal compound is an ammoniated complex compound of the aforesaid salts, and which are listed in U.S. Pat. No. 5,441,716, the degree of coordination is important in that it determines the cooling energy density potential as well as the mechanical ruggedness and integrity of the composite. Higher degrees of ammoniation tend to reduce the mechanical ruggedness and strength and the composites capability to serve as armor or protective matter. Where a greater amount of refrigerant is desired, a higher coordinated step product may be used, and for a reduced quantity of refrigerant, a lower coordination step may be suitable. The same holds true for complex compounds in which the refrigerant is other than ammonia. Similarly, where the refrigerant is water, and a hydrate is used, the amount of hydration may be selected to achieve the desired amount of water vapor available when the refrigerant is released. However, hydrates are more susceptible to losing mechanical integrity and strength with increased hydration level. The compromise between cooling energy density and mechanical strength and protective characteristics of the composite needs to be more carefully evaluated for each application than for ammoniated compounds.

If not previously sized, the material is cut to form layers of a desired size and/or shape, and each layer of metal compound bonded substrate material or multiple layers thereof are sealed by coating with a composition capable of preventing the penetration of gaseous refrigerant from the composite through the coating at ambient/atmospheric temperature and pressure and preventing water absorption by exposure to ambient atmospheric conditions, but which is capable of refrigerant penetration and release at a temperature increase that causes internal refrigerant partial pressure increase resulting in total internal pressure above exterior atmospheric or ambient pressure sufficient for the refrigerant to penetrate the coating. Typically, such total internal pressure will result in total pressures exceeding atmospheric pressure by about 15% or more. The coating step should be carried out under conditions or within a time so as to substantially seal the composite thereby preventing the complex compound or hydrated metal compound from deterioration by being exposed to atmospheric conditions which could cause liquefaction and/or loss of the salt bond and structural integrity of the product. As previously stated, the coating composition must be capable of preventing premature release of gaseous refrigerant from the composite at ambient temperatures and ambient atmospheric pressure. However, the coating composition must also allow for release and penetration of the refrigerant when the internal pressure of the composite is increased above the atmospheric/ambient pressure such as caused by the composite exposed to heat from fire, explosives, fuel combustion or caused by impact from shrapnel, bullets, projectiles, or other such events causing internal compound temperature and related pressure increase and resulting in the complex compound or metal hydroxide releasing the bonded refrigerant from the composite structure. The breached coating may vaporize, melt, fracture or otherwise become porous to the gaseous refrigerant released by the metal compound previously protected by the coating composition. Such coating must be configured to allow for such release or penetration of the gaseous refrigerant where the total internal pressure exceeds exterior ambient/atmospheric pressure (ΔP) by 15% or more up to even 500% or 1,000% or more. Typically, such ΔP will result at internal composite temperature of about 150° F. and preferably above about 200° F. or more or, in case of higher temperature ammoniated complex compounds or select hydrated compounds or hydroxides, such temperatures can exceed 500° F., 1,000° F. or even reach 2,000° F. Suitable coating compositions include epoxy resin, phenolic resin, neoprene, vinyl polymers such as PBC, PBC vinyl acetate or vinyl butyral copolymers, fluoroplastics such as polychlorotrifluoroethylene, polytetrafluoroethylene, FEP fluoroplastics, polyvinylidene fluoride, chlorinated rubber, and metal films including steel alloys, aluminum and zinc coatings. The aforesaid list is by way of example, and is not intended to be exhaustive. Again, the coating may be applied to individual layers of substrate, and/or to a plurality of layers or to the outer, exposed surfaces of a plurality or stack of substrate layers. When different sorbents and/or different refrigerants are used each such composition is preferably sealed by sealant to avoid undesired migration of refrigerant from one sorbent to the other or mixing or displacement of one refrigerant with the other,

Panels or other forms and geometries such as concave, convex or round shapes of the aforesaid coated substrate composites such as laminates are formed to the desired thickness. Moreover, such panels or laminates may also provide ballistic protection and may be installed in doors, sides, bottoms or tops of a vehicle, around ammunition, sensitive cargo, etc. to provide such protection as well as the above described cooling and fire extinguishing properties. Panels may also be shaped for other uses including personnel protection items and may be assembled in the form of cases, cylinders, boxes or containers for protection of ordnance, explosives, rockets, missiles, directed energy, such as laser beams or other materiel, fragile or sensitive items. Laminates may include layers of steel or other ballistic resistant material such as carbon fiber composites, aramid composites or metal alloys.

For composites mostly intended for non-ballistic and maximum thermal protection, additional refrigerant may be provided by incorporating spheres, compartments, packets or small reservoirs of pure liquid refrigerant or liquid refrigerant solutions in one or more layers, chambers or cavities with the most preferred refrigerant being water. The liquid containing layer or layers may be configured to release the liquid refrigerant or solution at the lowest temperature end the composite is designed and configured to provide protection for. The release of such refrigerants, e.g., water, ammonia, alcohols, amines, or refrigerant solution, e.g., alcohol-water, ammonia-water, aqueous brines, will occur when such a composite is exposed to elevated temperature causing internal refrigerant release and penetration, typically above 150° F. Such a modified composite must be designed to seal such liquid from the substrate/metal compound layers to prevent any such liquid from contacting, penetrating or permeating into the substrate under normal, typical ambient conditions. It is also important that the coating of adjacent layers prevents the released refrigerant from penetrating the coating and being reabsorbed onto the sorbent underneath the coating which would not only offset the cooling achieved via the evaporation of the refrigerant but adversely effect the system by generating the heat of absorption in the absorbing material thereby actually generating net heat due to exothermic reaction. If the composite incorporating such additional liquid refrigerant or refrigerant solution is to be used or exposed to conditions requiring ballistic protection, exterior panels, layers or other armor protection will be required to prevent exterior ballistic penetration of the composite. 

1. A composite configured to release refrigerant therefrom comprises a substrate material comprising polarized fibers of glass, polyamide, polyphenylene sulfide, carbon or graphite having bonded thereon a metal compound comprising a complex compound of a polar gaseous refrigerant and a metal salt and/or a hydrated metal hydroxide and/or a metal hydroxide of a metal selected from the group consisting of alkali metal, alkaline earth metal, transition metal, zinc, cadmium, tin, aluminum, or two or more thereof, at a concentration of at least about 0.3 grams/cc of open substrate material volume, and a coating composition thereon configured to prevent release of internal gaseous refrigerant therethrough at ambient temperatures and pressure and capable of penetration of gaseous refrigerant therethrough from the composite interior at temperatures causing total internal gas pressures of 15% or more above exterior pressure for such refrigerant release.
 2. A composite of claim 1 wherein said coating composition is a gas penetrable at internal/exterior atmospheric pressure ΔP of between about 15% and about 1,000%.
 3. A composite of claim 1 configured to release internal refrigerant at about 150° F. or more.
 4. A composite of claim 1 configured to release internal refrigerant at between about 200° F. and about 2,000° F.
 5. A composite of claim 1 wherein said refrigerant comprises ammonia, alcohol, amine, or water.
 6. A composite of claim 4 wherein said refrigerant comprises ammonia, alcohol, amine, or water.
 7. A composite of claim 1 wherein said metal salt comprises a halide, nitrate, nitrite, oxalate, perchlorate, sulfate or sulfite of one or more of said metals.
 8. A composite of claim 4 wherein said metal salt comprises a halide, nitrate, nitrite, oxalate, perchlorate, sulfate or sulfite of one or more of said metals.
 9. A composite of claim 6 wherein said metal salt comprises a halide, nitrate, nitrite, oxalate, perchlorate, sulfate or sulfite of one or more of said metals.
 10. A composite of claim 7 wherein said metal salt comprises a halide, nitrate, nitrite, oxalate, perchlorate, sulfate or sulfite of one or more of said metals.
 11. A composite of claim 9 wherein said complex compound comprises an ammoniated metal salt.
 12. A composite of claim 1 wherein said substrate comprises woven, layered or intertwined strands of said fibers.
 13. A composite of claim 1 comprising a plurality of layers of said substrate material and comprising two or more different complex compounds and/or different metal hydroxides and/or different hydrated metal hydroxides in respective different layers of said substrate material.
 14. A composite of claim 13 comprising two or more different complex compounds containing different polar refrigerants.
 15. A composite of claim 14 wherein said different refrigerants are ammonia and water.
 16. A composite of claim 1 configured to release refrigerant at different successively higher temperature ranges.
 17. A composite of claim 13 configured to release refrigerant at different successively higher temperature ranges.
 18. A composite of claim 14 configured to release different refrigerants at different successively higher temperature ranges.
 19. A composite of claim 15 configured to release different refrigerants at different successively higher temperature ranges.
 20. A composite of claim 17 wherein a first portion of said layers of said substrate have a first complex compound bonded thereon and a second portion of said layers of said substrate have a second complex compound bonded thereon.
 21. A composite of claim 20 wherein said first complex compound is ammoniated and said second complex compound is hydrated.
 22. A composite of claim 20 wherein a third portion of said layers of said substrate have a metal hydroxide bonded thereon.
 23. A composite of claim 21 wherein a third portion of said layers of said substrate have a metal hydroxide bonded thereon.
 24. A composite of claim 17 wherein a first portion of said layers of said substrate have a complex compound bonded thereon and a second portion of said layers of said substrate have a metal hydroxide bonded thereon.
 25. A composite of claim 1 configured to release refrigerant at successively higher temperatures comprising a plurality of layers of said substrate wherein different layers incorporate one or more complex compounds and/or one or more hydrated metal hydroxides and/or one or more metal hydroxides.
 26. A composite of claim 19 wherein said metal salt comprises a halide, nitrate, nitrite, oxalate, perchlorate, sulfate or sulfite of one or more of said metals.
 27. A composite of claim 20 wherein said metal salt comprises a halide, nitrate, nitrite, oxalate, perchlorate, sulfate or sulfite of one or more of said metals.
 28. A composite of claim 24 wherein said metal comprises a halide, nitrate, nitrite, oxalate, perchlorate, sulfate or sulfite of one or more of said metals.
 29. A composite of claim 25 wherein said metal comprises a halide, nitrate, nitrite, oxalate, perchlorate, sulfate or sulfite of one or more of said metals.
 30. A composite of claim 1 wherein said metal compound bridges adjacent strands and/or fibers of said substrate.
 31. A composite of claim 17 wherein said metal compound bridges adjacent strands and/or fibers of said substrate.
 32. A composite of claim 24 wherein said metal compound bridges adjacent strands and/or fibers of said substrate.
 33. A composite of claim 25 wherein said metal compound bridges adjacent strands and/or fibers of said substrate.
 34. A composite of claim 1 wherein said substrate material has an open volume of between about 30% and about 95%.
 35. A composite of claim 13 wherein said substrate material has an open volume of between about 30% and about 95%.
 36. A composite of claim 17 wherein said substrate material has an open volume of between about 30% and about 95%.
 37. A composite of claim 24 wherein said substrate material has an open volume of between about 30% and about 95%.
 38. A composite of claim 25 wherein said substrate material has an open volume of between about 30% and about 95%.
 39. A composite of claim 1 wherein said protective coating comprises an epoxy resin, phenolic resin, neoprene or vinyl polymer.
 40. A composite of claim 17 wherein each of said layers is coated.
 41. A composite of claim 17 wherein two or more of said plurality of layers are coated.
 42. A composite of claim 17 wherein only the exterior surface of said composite is coated.
 43. A composite of claim 24 wherein each of said layers is coated.
 44. A composite of claim 24 wherein two or more of said plurality of layers are coated.
 45. A composite of claim 24 wherein only the exterior surface of said composite is coated.
 46. A composite of claim 24 wherein the exterior surface of each of said plurality of substrate layers of said different metal compounds is coated.
 47. A composite of claim 25 wherein each of said layers is coated.
 48. A composite of claim 25 wherein two or more of said plurality of layers are coated.
 49. A composite of claim 25 wherein only the exterior surface of said composite is coated.
 50. A composite of claim 25 wherein the exterior surface of each of said plurality of substrate layers of said different metal compounds is coated.
 51. A composite of claim 25 comprising between two and six of said different layers wherein each different layer incorporates a different metal compound.
 52. A composite of claim 1 further incorporating one or more layers containing pure liquid refrigerant or liquid refrigerant solution sealed from contact or permeation thereof into the substrate under ambient temperature conditions.
 53. A method of preparing a composite configured to release refrigerant at above about 150° F. comprises: providing a substrate material comprising polarized fibers of glass, polyamide, polyphenylene sulfide, carbon or graphite; bonding on the surface thereof a metal compound comprising a metal salt or a metal hydroxide of a metal selected from the group consisting of alkali metal, alkaline earth metal, transition metal, zinc, cadmium, tin, aluminum, or two or more thereof, at a concentration of at least about 0.3 grams/cc of open substrate material volume; absorbing a polar gaseous refrigerant on said metal salt or water vapor on said metal hydroxide; forming layers of said metal compound bonded substrate material; and coating separate, multiple layers, or only the exterior surfaces of the composite with a coating composition configured to prevent penetration of gaseous refrigerant therethrough at ambient temperature and pressure and capable of penetration of internal gaseous refrigerant therethrough at temperatures causing total internal gas pressures of 15% or more above exterior atmospheric pressure.
 54. A method of preparing a composite configured to release refrigerants at progressively elevated temperatures comprising: providing a substrate material comprising polarized fibers of glass, polyamide, polyphenylene sulfide, carbon or graphite; bonding a first complex compound comprising a metal salt and a first polar gaseous refrigerant on a first portion of said substrate material at a concentration of at least about 0.3 gram/cc of open substrate material volume, said first complex compound capable of releasing said first refrigerant in a first temperature range, and forming one or more layers of said first portion of substrate material; bonding a second complex compound comprising a metal salt and a second polar gaseous refrigerant on a second portion of said substrate material at a concentration of at least about 0.3 gram/cc of open substrate material volume, said second complex compound capable of releasing said second refrigerant in a second temperature range, higher than said first temperature range, and forming one or more layers of said second portion of substrate material; coating said one or more layers of said first and second portions of substrate material and/or only the exterior surfaces of said composite with a coating composition configured to prevent penetration of gaseous refrigerant therethrough at ambient temperature and pressure and capable of penetration of internal gaseous refrigerant therethrough at temperatures causing total internal gas pressure of 15% or more above exterior atmospheric pressure; and laminating said first and second portions of coated substrate to form said composite.
 55. A method of preparing a composite configured to release different refrigerants at progressively elevated temperatures comprising: providing a substrate material comprising polarized fibers of glass, polyamide, polyphenylene sulfide, carbon or graphite; bonding one or more first complex compounds having one or more polar gaseous refrigerants on a first portion of said substrate material at a concentration of at least about 0.3 gram/cc of open substrate material volume, said first complex compound capable of releasing said first refrigerant on a first temperature range, and forming one or more layers of said first portion of substrate material; bonding a metal hydroxide or hydrated metal hydroxide on a second portion of said substrate material at a concentration of at least about 0.3 gram/cc of open substrate material volume, said second complex compound capable of releasing water vapor in a second temperature range, higher than said first temperature range, and forming one or more layers of said second portion of substrate material; coating said one or more layers of said first and second portions of substrate material and/or only the exterior surfaces of said composite with a coating composition configured to prevent penetration of gaseous refrigerant therethrough at ambient temperature and pressure and capable of penetration of internal gaseous refrigerant therethrough at temperatures causing total internal gas pressure of 15% or more above exterior atmospheric pressure; and laminating said first and second portions of coated substrate to form said composite.
 56. A method of preparing a composite configured to release gaseous refrigerant at progressively elevated temperatures comprising: providing a substrate material comprising polarized fibers of glass, polyamide, polyphenylene sulfide, carbon or graphite; bonding one or more complex compounds of metal salt and a polar gaseous refrigerant on a first portion of said substrate material at a concentration of at least about 0.3 gram/cc of open substrate material volume, said complex compounds capable of releasing said refrigerant in one or more first temperature ranges, and forming one or more layers of said first portion of substrate material; and/or bonding one or more hydrated metal hydroxides on a second portion of said substrate material at a concentration of at least about 0.3 gram/cc of open substrate material volume, said one or more hydrated metal hydroxides capable of releasing water in a second temperature range, higher than said first temperature ranges, and forming one or more layers of said second portion of substrate material; and/or bonding a metal hydroxide on a third portion of said substrate material at a concentration of at least about 0.3 grams/cc of open substrate material volume, said metal hydroxide capable of releasing water via conversion to a corresponding oxide in a third temperature range, higher than said first and second temperature range, and forming one or more layers of said third portion of substrate material; coating said one or more layers of said portions of substrate material and/or only the exterior surfaces of said composite with a coating composition configured to prevent penetration of gaseous refrigerant therethrough at ambient temperature and pressure and capable of penetration of internal gaseous refrigerant therethrough at temperatures causing total internal gas pressure of 15% or more above exterior atmospheric pressure; and laminating said first, second and third portions of coated substrate to form said composite.
 57. A method of preparing a composite configured to release gaseous refrigerant at progressively elevated temperatures comprising: providing a substrate material comprising polarized fibers of glass, polyamide, polyphenylene sulfide, carbon or graphite; bonding two or more different metal compounds selected from one or more different complex compounds of a metal salt and a polar gas refrigerant, and/or one or more hydrated metal hydroxides, and/or one or more metal hydroxides on two or more different layers, respectively, of said substrate material; coating said two or more different layers of said substrate material and/or only the exterior surfaces of said composite with a coating composition configured to prevent penetration of gaseous refrigerant therethrough at ambient temperature and pressure and capable of penetration of internal gaseous refrigerant therethrough at temperatures causing total internal gas pressure of 15% or more above exterior atmospheric pressure; and laminating said coated substrate layers to form said composite. 